asianflava wrote:Whew, that is pretty tight. What you may have to do is anneal a piece and bend it, then anneal it again and bend it some more. I played with different thicknesses and found 1/8 to work out OK, the thinner pieces would buckle.
But like I said, that radius looks pretty tight so I don't know if it would work.
I would have to agree. I do not see it possible to bend that radius even annealing it. I don't even think you could do it with a shrinker-stretcher. In order to bend that tight of a radius the metal need somewhere to go. You would need ti V-notch the inside side of the "T".
As far as where to get it, I am getting mine at a carpet store. I is soft enough to bend, but not that much.